C16200 Cadmium Copper (CDA 162)
Request a Quote

Shapes Available

C16200 Cadmium Copper (CDA 162)

SAE J461

C16200 Cadmium Copper alloy offers a unique combination of high tensile strength and high electrical conductivity for an industry where these properties are generally considered incompatible. The nominal composition of 99.0% copper and 1.0% cadmium can lead to these unique properties.

Typical Application for C16200 Cadmium Copper alloys:

Electrical Industry: Resistance Welding Electrodes, Circuit Breaker Switches, Stud Bases for Power Transmitters, Electrical Conductor Material

Consumer: Rod Extensions, Pencil-type, Light Soldering Guns, Tips

Industrial: Connectors, Solderless Wrapped, Welding Wheels, Trolley Wires

Specifications

Product Type Temper Type
Bar SAE J461, J463
Forgings SAE J461, J463
Rod SAE J461, J463
Wire AMS B624, B105 Military MIL-W-82598

Al Be Cd Cu Fe
Min/Max - - 07-1.2 Rem .02
Nominals - - 1.0 99.0 -
Temper Sect. Size Cold Work Type Min Temp Tensile Strength YS
0.05% UL
YS
0.02% Offset
YS
0.005% Offset
Elong. RH
B
RH
C
RH
F
RH
30T
VH
500
BH
500
BH
3000
Shear
Strgth
Fatigue
Strgth
Izod
Impact
Strgth
- in. % - F ksi ksi ksi ksi % B C F 30T 500 500 3000 ksi ksi ft-lb
- mm. - - C MPa MPa MPa MPa - - - - - - - - MPa MPa J
FLAT PRODUCTS
H10 0.04 0 TYP 68 72 59 - - 1 75 - - - - - - - - 0.0
̴Ì_ 1 ̴Ì_ ̴Ì_ 20 496 407 - - 1 75 - - - - - - - - 0.0
H04 0.04 0 TYP 68 60 45 - - 5 64 - - - - - - - - 0.0
̴Ì_ 1 ̴Ì_ ̴Ì_ 20 414 310 - - 5 64 - - - - - - - - 0.0
OS025 0.04 0 TYP 68 35 11 - - 52 - - 54 - - - - - - 0.0
̴Ì_ 1 ̴Ì_ ̴Ì_ 20 241 76 - - 52 - - 54 - - - - - - 0.0
H08 0.04 0 TYP 68 64 - - - 3 73 - - - - - - - - 0.0
̴Ì_ 1 ̴Ì_ ̴Ì_ 20 411 - - - 3 73 - - - - - - - - 0.0
ROD
OS050 0.5 0 TYP 68 35 7 6 - 56 - - 46 - - - - 27 15 0.0
̴Ì_ 12.7 ̴Ì_ ̴Ì_ 20 241 48 47 - 56 - - 46 - - - - 186 100 0.0
OS025 0.5 0 TYP 68 36 12 - - 57 - - 46 - - - - - - 0.0
̴Ì_ 12.7 ̴Ì_ ̴Ì_ 20 248 83 - - 57 - - 46 - - - - - - 0.0
H02 0.5 25 TYP 68 58 45 - - 12 65 - - - - - - - - 0.0
̴Ì_ 12.7 ̴Ì_ ̴Ì_ 20 400 310 - - 12 65 - - - - - - - - 0.0
H04 0.5 0 TYP 68 73 69 70 - 9 73 - - - - - - 56 30 0.0
̴Ì_ 12.7 ̴Ì_ ̴Ì_ 20 503 474 483 - 9 73 - - - - - - 386 207 0.0
WIRE
H08 0.08 0 TYP 68 80 66 - - 2 - - - - - - - - - 0.0
̴Ì_ 2 ̴Ì_ ̴Ì_ 20 552 455 - - 2 - - - - - - - - - 0.0
OS025 0.08 0 TYP 68 38 12 - - 50 - - - - - - - - - 0.0
̴Ì_ 2 ̴Ì_ ̴Ì_ 20 262 83 - - 50 - - - - - - - - - 0.0
H80 0.01 99 TYP 68 100 - - - 1 - - - - - - - - - 0.0
̴Ì_ 0.25 ̴Ì_ ̴Ì_ 20 689 - - - 1 - - - - - - - - - 0.0
H80 0.08 96 TYP 68 88 - - - 1 - - - - - - - - - 0.0
̴Ì_ 2 ̴Ì_ ̴Ì_ 20 607 - - - 1 - - - - - - - - - 0.0
H04 0.08 0 TYP 68 70 55 - - 6 - - - - - - - - - 0.0
̴Ì_ 2 ̴Ì_ ̴Ì_ 20 483 379 - - 6 - - - - - - - - - 0.0
Product Property US Customary Metric
Melting Point - Liquidus 1969 F 1076 C
Melting Point - Solidus 1886 F 1030 C
Density 0.321 lb/in3 at 68 F 8.89 gm/cm3 @ 20 C
Specific Gravity 8.890 8.89
Electrical Resistivity 11.50 ohms-cmil/ft @ 68 F 1.91 microhm-cm @ 20 C
Electrical Conductivity 90 % IACS @ 68 F 0.527 MegaSiemens/cm @ 20 C
Thermal Conductivity 208 Btu . ft/(hr . ft2.oF)at 68F 360.0 W/m .å¡K at 20 C
Modulas of Elasticity in Tension 17000 ksi 117000 MPa
Modulus of Rigidity 6400 ksi 44130 MPa
Specific Heat Capacity 0.090 Btu/lb/å¡F at 68 F 377.1 J/kg . å¡K at 293 K
Joining Technique Suitability
Brazing Excellent
Butt Weld Good
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Good
Coated Metal Arc Welding Not Recommended
Gas Sheilded Arc Welding Good
Machinability rating 20
Oxyacetylene Welding Good
Seam Weld Not Recommended
Soldering Excellent
Spot Weld Not Recommended