Pipe
Typical Uses for C92900 Leaded Nickel Tin Bronze
- Industrial: General Service Bearings, Pump Bodies, Impellers for Mine Water, Wear Plates, Cams, Gears, Worm Gears
Product Specifications
| End Product | Specification |
| Centrifugal | ASTM B427 |
| Continuous | ASTM B505, SAE J461, J462 |
| Ingot | ASTM B30 |
| Sand | ASTM B427, SAE J462, J461 |
Chemical Composition
| Al | Sb | Cu | Fe | Pb | Ni | P | Si | S | Sn | Zn | |
| Min/Max | 0.005 | 0.25 | 82.0 - 86.0 | 0.2 | 2.0 - 3.2 | 2.8 - 4.0 | 0.05 | 0.005 | 0.05 | 9.0 - 11.0 | 0.25 |
| Nominals | - | - | 84.0000 | - | 2.6000 | 3.4000 | - | - | - | 10.0000 | - |
Temper
| Product Type | Temper Type |
| Centrifugal | ASTM B427 |
| Continuous | ASTM B505, SAE J461, J462 |
| Ingot | ASTM B30 |
| Sand | ASTM B427, SAE J462, J461 |
Mechanical Properties
| Temper | Sect. Size | Cold Work | Type Min | Temp | Tensile Strength | YS 0.05% UL |
YS 0.02% Offset |
YS 0.005% Offset |
Elong. | RH B |
RH C |
RH F |
RH 30T |
VH 500 |
BH 500 |
BH 3000 |
Shear Strgth |
Fatigue Strgth |
Izod Impact Strgth |
| - | in. | % | - | F | ksi | ksi | ksi | ksi | % | B | C | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb |
| - | mm. | - | - | C | MPa | MPa | MPa | MPa | - | - | - | - | - | - | - | - | MPa | MPa | J |
| As Continous Cast | |||||||||||||||||||
| M07 | 68 | 45 | 25 | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| M07 | 0 | SMIN | 20 | 310 | 172 | - | - | 8 | - | - | - | - | - | - | - | - | - | 0 | |
| As Permanent Mold Cast | |||||||||||||||||||
| M05 | 68 | 47 | 26 | - | - | - | - | - | - | - | - | - | - | - | - | 12 | |||
| M05 | 0 | TYP | 20 | 324 | 179 | - | - | 20 | - | - | - | - | - | 80 | - | - | - | 16 | |
| As Sand Cast | |||||||||||||||||||
| M01 | 68 | 47 | 26 | - | - | - | - | - | - | - | - | - | - | - | - | 12 | |||
| M01 | 0 | TYP | 20 | 324 | 179 | - | - | 20 | - | - | - | - | - | 80 | - | - | - | 16 | |
| M01 | 68 | 45 | 25 | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| M01 | 0 | SMIN | 20 | 310 | 172 | - | - | 8 | - | - | - | - | - | 75 | - | - | - | 0 |
Physical Properties
| Product Property | US Customary | Metric |
| Coefficient of Thermal Expansion | 9.5 · 10-6 per oF (68-392 F) | 17.1 · 10-6 per oC (20-200 C) |
| Density | 0.32 lb/in3 at 68 F | 8.86 gm/cm3 @ 20 C |
| Electrical Conductivity | 9 %IACS @ 68 F | 0.053 MegaSiemens/cm @ 20 C |
| Electrical Resistivity | 113.5 ohms-cmil/ft @ 68 F | 18.87 microhm-cm @ 20 C |
| Incipient Melting | 600 oF | 316 C |
| Melting Point - Liquidus | 1887 F | 1031 C |
| Melting Point - Solidus | 1575 F | 857 C |
| Modulas of Elasticity in Tension | 14000 ksi | 96500 |
| Specific Gravity | 8.86 | 8.86 |
| Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg · oK at 293 K |
| Thermal Conductivity | 33.6 Btu · ft/(hr · ft2 · oF) at 68F | 58.2 W/m · oK at 20 C |
Fabrication
| Joining Technique | Suitability |
| Brazing | Good |
| Coated Metal Arc Welding | Not Recommended |
| Gas Shielded Arc Welding | Not Recommended |
| Machinability Rating | 40 |
| Oxyacetylene Welding | Not Recommended |
| Soldering | Excellent |
Our Services
40+ years of experience
Aviva Metals Houston warehouse operation is a AS9120B, and AS9100D in our Ohio foundry, based on ISO 9001:2015. We are now also offering our complete range of brass, bronze and copper alloys in precision machined or milled parts, in full accordance with your drawings. Aviva Metals creates custom precision bearings and bushings, flanges, washers, double flange bearings, full half bearings, spacers and special machined parts that can be shipped on a global basis and in full accordance with most international standards.