Pipe
Sheet/Plate
Typical Uses for C61300
- Building: Wire Screening, Fasteners, Bolts, Nuts
- Industrial : Heat Exchanger Tube, Seamless Tubing and Pipe, Tube Sheets, Columns, Sea Water Piping, Mining Shovels, Tie Rods, Condenser Tube, Water Boxes, Corrosion Resistant Vessels, Machine Parts, Piping Systems, Acid Resistant, Gaskets, Tanks, Desalination Equipment
- Marine: Marine Hardware, Protective Sheathing Ordnance, Mixing Troughs, Blending Chambers
- Other : Ball Valve Seats
Product Specifications
| End Product | Specification |
| Bar | ASTM B150, B169 FEDERAL QQ-C-450 |
| Pipe | ASTM B315 |
| Pipe, Welded | ASTM B608 |
| Plate | ASTM B169 FEDERAL QQ-C-450 |
| Plate, Bridge and Bearing | ASTM B100 |
| Plate, Clad | ASTM B432 |
| Plate, Condenser Tube | ASTM B171, B171 |
| Rod | ASTM B150 |
| Shapes | ASTM B150 |
| Sheet | ASTM B169 FEDERAL QQ-C-450 |
| Strip | ASTM B169 FEDERAL QQ-C-450 |
| Tube | ASTM B315 |
| Tube, Condensor | ASTM B111 |
Chemical Composition
| Cu | Al | Fe | Pb | Mn | Ni | P | Si | Sn | Zn | |
| Min./Max. | Rem. | 6.0-7.5 | 2.0-3.0 | .01 | .20 | .15 | .015 | .10 | .20-.50 | .10 |
| Nominal | 90.3 | 6.8 | 2.5 | - | - | - | - | - | .35 | - |
Temper
| Flat Products | - |
| BAR, DRAWN | H04, H58 |
| BAR, ROLLED | O60 |
| PLATE | M20, O60, OS025, OS050 |
| SHEET | O60 |
| Other | |
| PIPE | M30, O60 |
| ROD | H58 |
| SHAPES | H58, M30 |
| TUBE | O60 |
Mechanical Properties
| Temper | Sect. Size | Cold Work | Type Min | Temp | Tensile Strength | YS 0.05% UL |
YS 0.02% Offset |
YS 0.005% Offset |
Elong. | RH B |
RH C |
RH F |
RH 30T |
VH 500 |
BH 500 |
BH 3000 |
Shear Strgth |
Fatigue Strgth |
Izod Impact Strgth |
| - | in. | % | - | F | ksi | ksi | ksi | ksi | % | B | C | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb |
| - | mm. | - | - | C | MPa | MPa | MPa | MPa | - | - | - | - | - | - | - | - | MPa | MPa | J |
| Flat Products | |||||||||||||||||||
| O60 | 3 | 0 | TYP | 68 | 70 | 30 | - | - | 40 | 78 | - | - | - | - | - | - | 42 | 21 | 0.0 |
| 76 | 20 | 483 | 207 | - | - | 40 | 78 | - | - | - | - | - | - | 290 | 145 | 0.0 | |||
| O60 | 1 | 0 | TYP | 68 | 76 | 33 | - | - | 42 | 79 | - | - | - | - | - | - | 45 | 25 | 0.0 |
| 25.4 | 20 | 524 | 228 | - | - | 42 | 79 | - | - | - | - | - | - | 310 | 172 | 0.0 | |||
| O60 | 0.125 | 0 | TYP | 68 | 80 | 40 | - | - | 40 | 82 | - | - | - | - | - | - | 52 | 28 | 0.0 |
| 3.18 | 20 | 552 | 276 | - | - | 40 | 82 | - | - | - | - | - | - | 359 | 193 | 0.0 | |||
| Rod | |||||||||||||||||||
| H04 | 1 | 25 | TYP | 68 | 82 | 55 | - | - | 35 | 90 | - | - | - | - | - | - | 45 | - | 0.0 |
| 25.4 | 20 | 565 | 379 | - | - | 35 | 90 | - | - | - | - | - | - | 310 | - | 0.0 | |||
| H04 | 2 | 25 | TYP | 68 | 80 | 48 | - | - | 35 | 88 | - | - | - | - | - | - | 40 | - | 0.0 |
| 51 | 20 | 552 | 331 | - | - | 35 | 88 | - | - | - | - | - | - | 276 | - | 0.0 | |||
| H04 | 0.5 | 25 | TYP | 68 | 85 | 58 | - | - | 35 | 91 | - | - | - | - | - | - | 48 | - | 0.0 |
| 12.7 | 20 | 586 | 400 | - | - | 35 | 91 | - | - | - | - | - | - | 331 | - | 0.0 | |||
| Flat Products | |||||||||||||||||||
| O60 | 0.5 | 0 | TYP | 68 | 78 | 35 | - | - | 42 | 81 | - | - | - | - | - | - | 50 | 26 | 0.0 |
| 12.7 | 20 | 538 | 241 | - | - | 42 | 81 | - | - | - | - | - | - | 345 | 179 | 0.0 | |||
| Plate | |||||||||||||||||||
| O60 | 1 | 0 | TYP | 68 | 52 | 17 | - | - | 45 | 60 | - | - | - | - | - | - | - | - | 0.0 |
| 25.4 | 20 | 359 | 117 | - | - | 45 | 60 | - | - | - | - | - | - | - | - | 0.0 |
Physical Properties
| Product Property | US Customary | Metric |
| Melting Point - Liquidus | 1915 F | 1046 C |
| Melting Point - Solidus | 1905 F | 1041 C |
| Density | 0.287 lb/in3 at 68 F | 7.95 gm/cm3 @ 20 C |
| Specific Gravity | 7.950 | 7.95 |
| Electrical Resistivity | 86.80 ohms-cmil/ft @ 68 F | 14.43 microhm-cm @ 20 C |
| Electrical Conductivity | 12 %IACS @ 68 F | 0.07 MegaSiemens/cm @ 20 C |
| Thermal Conductivity | 32 Btu · ft/(hr · ft2 · oF) at 68F | 55.4 W/m · oK at 20 C |
| Coefficient of Thermal Expansion | 9 . 10-6 per oF (68-572 F) | 16.2 . 10-6 per oC (20-300 C) |
| Specific Heat Capacity | 0.090 Btu/lb/oF at 68 F | 377.1 J/kg · oK at 293 K |
| Modulas of Elasticity in Tension | 17000 ksi | 117000 MPa |
| Modulus of Rigidity | 6400 ksi | 44130 MPa |
Fabrication
| Joining Technique | Suitability |
| Soldering | Not Recommended |
| Brazing | Fair |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Excellent |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Seam Weld | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Good |
| Forgeability Rating | 50 |
| Machinability Rating | 30 |
Our Services
40+ years of experience
Aviva Metals Houston warehouse operation is a AS9120B, and AS9100D in our Ohio foundry, based on ISO 9001:2015. We are now also offering our complete range of brass, bronze and copper alloys in precision machined or milled parts, in full accordance with your drawings. Aviva Metals creates custom precision bearings and bushings, flanges, washers, double flange bearings, full half bearings, spacers and special machined parts that can be shipped on a global basis and in full accordance with most international standards.