C27000 Yellow Brass 65% (CDA 270)
ASTM B134, SAE J461
Hot-forms more readily and is stronger than C26000.
Tube
Wire
Typical Uses for C27000 Yellow Brass "65%"
- Architecture: Handrails, Grillwork
- Automotive: Tanks, Radiator Cores
- Builders Hardware: Push Plates, Finish Hardware, Hinges, Stencils, Kick Plates, Locks
- Electrical: Socket Shells, Screw Shells, Reflectors, Lamp Fixtures, Flashlight Shells
- Fasteners: Grommets, Eyelets, Screws, Rivets, Fasteners, Pins
- Industrial: Bead Chain, Springs, Chain
- Marine: Fasteners
- Plumbing: Sink Strainers, Plumbing Accessories
Product Specifications
| End Product | Specification |
| Bolt | ASTM F468 |
| Nuts | ASTM F467 |
| Rod | SAE J463, J461 |
| Screws | ASTM F468 |
| Studs | ASTM F468 |
| Tube | ASTM B135 |
| Tube, Welded | ASTM B587 |
| Wire | AMS 4712, 4713, ASTM B134, SAE J463, J461 |
| Wire, Tinned | AMS 4710 |
Chemical Composition
| Cu | Fe | Pb | Zn | |
| Min/Max | 63.0 - 68.5 | 0.07 | 0.09 | Rem |
| Nominals | 65.0000 | - | - | 35.0000 |
Temper
| Product Type | Temper Type |
| Bolt | ASTM F468 |
| Nuts | ASTM F467 |
| Rod | SAE J463, J461 |
| Screws | ASTM F468 |
| Studs | ASTM F468 |
| Tube | ASTM B135 |
| Tube, Welded | ASTM B587 |
| Wire | AMS 4712, 4713, ASTM B134, SAE J463, J461 |
| Wire, Tinned | AMS 4710 |
Mechanical Properties
| Temper | Sect. Size | Cold Work | Type Min | Temp | Tensile Strength | YS 0.05% UL |
YS 0.02% Offset |
YS 0.005% Offset |
Elong. | RH B |
RH C |
RH F |
RH 30T |
VH 500 |
BH 500 |
BH 3000 |
Shear Strgth |
Fatigue Strgth |
Izod Impact Strgth |
| - | in. | % | - | F | ksi | ksi | ksi | ksi | % | B | C | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb |
| - | mm. | - | - | C | MPa | MPa | MPa | MPa | - | - | - | - | - | - | - | - | MPa | MPa | J |
| FLAT PRODUCTS | |||||||||||||||||||
| H02 | 0.04 | 68 | 61 | 50 | - | - | - | - | - | - | - | - | - | - | 40 | - | |||
| H02 | 1 | 0 | TYP | 20 | 421 | 345 | - | - | 23 | 70 | - | - | 65 | - | - | - | 276 | - | 0 |
| OS015 | 0.04 | 68 | 53 | 22 | - | - | - | - | - | - | - | - | - | - | - | - | |||
| OS015 | 1 | 0 | TYP | 20 | 365 | 152 | - | - | 54 | - | - | 78 | 43 | - | - | - | - | - | 0 |
| H06 | 0.04 | 68 | 85 | 62 | - | - | - | - | - | - | - | - | - | - | 45 | - | |||
| H06 | 1 | 0 | TYP | 20 | 586 | 427 | - | - | 5 | 87 | - | - | 74 | - | - | - | 310 | - | 0 |
| OS035 | 0.04 | 68 | 49 | 17 | - | - | - | - | - | - | - | - | - | - | 34 | - | |||
| OS035 | 1 | 0 | TYP | 20 | 338 | 117 | - | - | 57 | - | - | 68 | 31 | - | - | - | 234 | - | 0 |
| H04 | 0.04 | 68 | 74 | 60 | - | - | - | - | - | - | - | - | - | - | 43 | 14 | |||
| H04 | 1 | 0 | TYP | 20 | 510 | 414 | - | - | 8 | 80 | - | - | 70 | - | - | - | 296 | 97 | 0 |
| H08 | 0.04 | 68 | 91 | 62 | - | - | - | - | - | - | - | - | - | - | 47 | 20 | |||
| H08 | 1 | 0 | TYP | 20 | 627 | 427 | - | - | 3 | 90 | - | - | 76 | - | - | - | 324 | 138 | 0 |
| OS070 | 0.04 | 68 | 46 | 14 | - | - | - | - | - | - | - | - | - | - | 32 | 12 | |||
| OS070 | 1 | 0 | TYP | 20 | 317 | 97 | - | - | 65 | - | - | 58 | 15 | - | - | - | 221 | 83 | 0 |
| OS050 | 0.04 | 68 | 47 | 15 | - | - | - | - | - | - | - | - | - | - | - | - | |||
| OS050 | 1 | 0 | TYP | 20 | 324 | 103 | - | - | 62 | - | - | 64 | 26 | - | - | - | - | - | 0 |
| H01 | 0.04 | 68 | 54 | 40 | - | - | - | - | - | - | - | - | - | - | 36 | - | |||
| H01 | 1 | 0 | TYP | 20 | 372 | 276 | - | - | 43 | 55 | - | - | 54 | - | - | - | 248 | - | 0 |
| H00 | 0.04 | 68 | 50 | 35 | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H00 | 1 | 0 | TYP | 20 | 345 | 241 | - | - | 50 | 50 | - | - | 50 | - | - | - | - | - | 0 |
| OS025 | 0.04 | 68 | 51 | 19 | - | - | - | - | - | - | - | - | - | - | - | - | |||
| OS025 | 1 | 0 | TYP | 20 | 352 | 131 | - | - | 55 | - | - | 72 | 36 | - | - | - | - | - | 0 |
| ROD | |||||||||||||||||||
| H00 | 1 | 68 | 55 | 40 | - | - | - | - | - | - | - | - | - | - | 36 | - | |||
| H00 | 25.4 | 6 | TYP | 20 | 379 | 276 | - | - | 48 | 55 | - | - | - | - | - | - | 248 | - | 0 |
| OS050 | 1 | 68 | 48 | 16 | - | - | - | - | - | - | - | - | - | - | 34 | - | |||
| OS050 | 25.4 | 0 | TYP | 20 | 331 | 110 | - | - | 65 | - | - | 65 | - | - | - | - | 234 | - | 0 |
| WIRE | |||||||||||||||||||
| H01 | 0.08 | 68 | 70 | - | - | - | - | - | - | - | - | - | - | - | 42 | 22 | |||
| H01 | 2 | 0 | TYP | 20 | 483 | - | - | - | 20 | - | - | - | - | - | - | - | 290 | 152 | 0 |
| H00 | 0.08 | 68 | 58 | - | - | - | - | - | - | - | - | - | - | - | 38 | - | |||
| H00 | 2 | 0 | TYP | 20 | 400 | - | - | - | 35 | - | - | - | - | - | - | - | 262 | - | 0 |
| H04 | 0.08 | 68 | 110 | - | - | - | - | - | - | - | - | - | - | - | 55 | - | |||
| H04 | 2 | 0 | TYP | 20 | 758 | - | - | - | 8 | - | - | - | - | - | - | - | 379 | - | 0 |
| H02 | 0.08 | 68 | 88 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H02 | 2 | 0 | TYP | 20 | 607 | - | - | - | 15 | - | - | - | - | - | - | - | - | - | 0 |
| H06 | 0.08 | 68 | 120 | - | - | - | - | - | - | - | - | - | - | - | 60 | - | |||
| H06 | 2 | 0 | TYP | 20 | 827 | - | - | - | 4 | - | - | - | - | - | - | - | 414 | - | 0 |
| H08 | 0.08 | 68 | 128 | - | - | - | - | - | - | - | - | - | - | - | 60 | - | |||
| H08 | 2 | 0 | TYP | 20 | 883 | - | - | - | 3 | - | - | - | - | - | - | - | 414 | - | 0 |
| OS035 | 0.08 | 68 | 50 | - | - | - | - | - | - | - | - | - | - | - | 34 | - | |||
| OS035 | 2 | 0 | TYP | 20 | 345 | - | - | - | 60 | - | - | - | - | - | - | - | 234 | - | 0 |
Physical Properties
| Product Property | US Customary | Metric |
| Coefficient of Thermal Expansion | 11.3 · 10-6 per oF (68-572 F) | 20.3 · 10-6 per oC (20-300 C) |
| Density | 0.306 lb/in3 @ 68 F | 8.47 gm/cm3 @ 20 C |
| Electrical Conductivity | 27 %IACS @ 68 F | 0.158 MegaSiemens/cm @ 20 C |
| Electrical Resistivity | 38.4 ohms-cmil/ft @ 68 F | 6.38 microhm-cm @ 20 C |
| Melting Point Liquid US | 1710 F | 932 C |
| Melting Point Solid US | 1660 F | 904 C |
| Modulas of Elasticity in Tension | 15000 ksi | 103400 MPa |
| Modulas of Rigidity | 5600 ksi | 38610 Mpa |
| Specific Gravity | 8.47 | 8.47 |
| Specific Heat Capacity | 0.09 Btu/lb/oF @ 68 F | 377.1 J/kg · oK at 293 K |
| Thermal Conductivity | 67.0 Btu · ft/(hr · ft2 · oF) @ 68 F | 116.0 W/m · oK at 20 C |
Fabrication
| Joining Technique | Suitability |
| Brazing | Excellent |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Excellent |
| Capacity for Being Hot Formed | Poor |
| Coated Metal Arc Welding | Not recommended |
| Gas Sheilded Arc Welding | Fair |
| Machinability rating | 30 |
| Oxyacetylene Welding | Good |
| Seam Weld | Not recommended |
| Soldering | Excellent |
| Spot Weld | Good |
Our Services
40+ years of experience
Aviva Metals Houston warehouse operation is a AS9120B, and AS9100D in our Ohio foundry, based on ISO 9001:2015. We are now also offering our complete range of brass, bronze and copper alloys in precision machined or milled parts, in full accordance with your drawings. Aviva Metals creates custom precision bearings and bushings, flanges, washers, double flange bearings, full half bearings, spacers and special machined parts that can be shipped on a global basis and in full accordance with most international standards.