Typical Uses for C53400 Phosphor Bronze "B-1"
- Industrial: Bushings, Bearings, Fasteners
Product Specifications
| End Product | Specification |
| Bar | ASTM B103, B139 |
| Bearings and Bushings | MILITARY MIL-B-13501 |
| Plate | ASTM B103 |
| Rod | ASTM B139 |
| Shapes | ASTM B139 |
| Sheet | ASTM B103 |
| Strip | ASTM B103 |
Chemical Composition
| Cu | Fe | Pb | P | Sn | Zn | |
| Min/Max | Rem | 0.1 | 0.8 - 1.2 | 0.03 - 0.35 | 3.5 - 5.8 | 0.3 |
| Nominals | 94.2000 | - | 1.0000 | 0.1900 | 4.6000 | - |
Temper
| Product Type | Temper Type |
| Bar | ASTM B103, B139 |
| Bearings and Bushings | MILITARY MIL-B-13501 |
| Plate | ASTM B103 |
| Rod | ASTM B139 |
| Shapes | ASTM B139 |
| Sheet | ASTM B103 |
| Strip | ASTM B103 |
Mechanical Properties
| Temper | Sect. Size | Cold Work | Type Min | Temp | Tensile Strength | YS 0.05% UL |
YS 0.02% Offset |
YS 0.005% Offset |
Elong. | RH B |
RH C |
RH F |
RH 30T |
VH 500 |
BH 500 |
BH 3000 |
Shear Strgth |
Fatigue Strgth |
Izod Impact Strgth |
| - | in. | % | - | F | ksi | ksi | ksi | ksi | % | B | C | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb |
| - | mm. | - | - | C | MPa | MPa | MPa | MPa | - | - | - | - | - | - | - | - | MPa | MPa | J |
| BAR | |||||||||||||||||||
| H02 | 0 | 68 | 70 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H02 | 0 | 0 | SMAX | 20 | 483 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| O60 | 0 | 68 | 55 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| O60 | 0 | 0 | SMAX | 20 | 380 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H08 | 0 | 68 | 104 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H08 | 0 | 0 | SMAX | 20 | 720 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H06 | 0 | 68 | - | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| H06 | 0 | 0 | TYP | 20 | - | - | - | - | 91 | - | - | - | - | - | - | - | - | 0 | |
| H06 | 0 | 68 | 99 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H06 | 0 | 0 | SMAX | 20 | 685 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H02 | 0 | 68 | 55 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H02 | 0 | 0 | SMIN | 20 | 380 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| M20 | 0 | 68 | 60 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| M20 | 0 | 0 | SMAX | 20 | 415 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H02 | 0 | 68 | - | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| H02 | 0 | 0 | TYP | 20 | - | - | - | - | 70 | - | - | - | - | - | - | - | - | 0 | |
| H10 | 0 | 68 | 109 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H10 | 0 | 0 | SMAX | 20 | 750 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H04 | 0 | 68 | 72 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H04 | 0 | 0 | SMIN | 20 | 496 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| O60 | 0 | 68 | 40 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| O60 | 0 | 0 | SMIN | 20 | 275 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| O60 | 0 | 68 | - | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| O60 | 0 | 0 | TYP | 20 | - | - | - | - | 28 | - | - | - | - | - | - | - | - | 0 | |
| M20 | 0 | 68 | 40 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| M20 | 0 | 0 | SMIN | 20 | 275 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H10 | 0 | 68 | - | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| H10 | 0 | 0 | TYP | 20 | - | - | - | - | 94 | - | - | - | - | - | - | - | - | 0 | |
| H08 | 0 | 68 | 91 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H08 | 0 | 0 | SMIN | 20 | 625 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H04 | 0 | 68 | 87 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H04 | 0 | 0 | SMAX | 20 | 600 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H08 | 0 | 68 | - | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| H08 | 0 | 0 | TYP | 20 | - | - | - | - | 94 | - | - | - | - | - | - | - | - | 0 | |
| H06 | 0 | 68 | 84 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H06 | 0 | 0 | SMIN | 20 | 580 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
| H04 | 0 | 68 | - | - | - | - | - | - | - | - | - | - | - | - | - | ||||
| H04 | 0 | 0 | TYP | 20 | - | - | - | - | 86 | - | - | - | - | - | - | - | - | 0 | |
| FLAT PRODUCTS | |||||||||||||||||||
| H06 | 0 | 68 | 91 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H06 | 0 | 0 | TYP | 20 | 627 | - | - | - | - | 91 | - | - | - | - | - | - | - | - | 0 |
| H08 | 0 | 68 | 98 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H08 | 0 | 0 | TYP | 20 | 676 | - | - | - | - | 94 | - | - | - | - | - | - | - | - | 0 |
| H04 | 0 | 68 | 80 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H04 | 0 | 0 | TYP | 20 | 552 | - | - | - | - | 86 | - | - | - | - | - | - | - | - | 0 |
| H02 | 0 | 68 | 62 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H02 | 0 | 0 | TYP | 20 | 427 | - | - | - | - | 70 | - | - | - | - | - | - | - | - | 0 |
| O60 | 0 | 68 | 47 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| O60 | 0 | 0 | TYP | 20 | 324 | - | - | - | - | 28 | - | - | - | - | - | - | - | - | 0 |
| H10 | 0 | 68 | 102 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| H10 | 0 | 0 | TYP | 20 | 703 | - | - | - | - | 94 | - | - | - | - | - | - | - | - | 0 |
| M20 | 0 | 68 | 49 | - | - | - | - | - | - | - | - | - | - | - | - | - | |||
| M20 | 0 | 0 | TYP | 20 | 338 | - | - | - | - | - | - | - | - | - | - | - | - | - | 0 |
Physical Properties
| Product Property | US Customary | Metric |
| Coefficient of Thermal Expansion | 9.9 · 10-6 per oF (68-572 F) | 17.14 · 10-6 per oC (20-300 C) |
| Density | 0.322 lb/in3 @ 68 F | 8.91 gm/cm3 @ 20 C |
| Electrical Conductivity | 15 %IACS @ 68 F | 0.087 MegaSiemens/cm @ 20 C |
| Electrical Resistivity | 69.1 ohms-cmil/ft @ 68 F | 11.4 microhm-cm @ 20 C |
| Melting Point Liquid US | 1620 F | 1049 C |
| Melting Point Solid US | 1750 F | 954 C |
| Modulas of Elasticity in Tension | 16000 ksi | 110300 MPa |
| Modulas of Rigidity | 6000 ksi | 41300 MPa |
| Specific Gravity | 8.91 | 8.91 |
| Thermal Conductivity | 40.0 Btu · ft/(hr · ft2 · oF) @ 68 F | 69.28 W/m · oK at 20 C |
Fabrication
| Joining Technique | Suitability |
| Brazing | Good |
| Butt Weld | Good |
| Capacity for Being Cold Worked | Good |
| Capacity for Being Hot Formed | Poor |
| Coated Metal Arc Welding | Poor |
| Gas Sheilded Arc Welding | Fair |
| Machinability rating | 70 |
| Oxyacetylene Welding | Poor |
| Seam Weld | Fair |
| Soldering | Excellent |
| Spot Weld | Fair |
Our Services
40+ years of experience
Aviva Metals Houston warehouse operation is a AS9120B, and AS9100D in our Ohio foundry, based on ISO 9001:2015. We are now also offering our complete range of brass, bronze and copper alloys in precision machined or milled parts, in full accordance with your drawings. Aviva Metals creates custom precision bearings and bushings, flanges, washers, double flange bearings, full half bearings, spacers and special machined parts that can be shipped on a global basis and in full accordance with most international standards.