C70600 Copper Nickel (90/10)
C70600 (C706) & C71500 (C715), Copper nickel offers excellent corrosion resistance, especially in marine salt water environments. The main, wrought copper-nickel alloys chosen for sea water service contain 10 or 30 percent nickel. They also have important additions of iron and manganese which are necessary to maintain good corrosion resistance. Some of the primary uses for C706 include copper nickel fittings (CuNi Fittings) as well as condensers and exchanger shells.

Standards | ASTM B-151, ASTM B-122, DIN 2.0872 |
KS D5301 | C7060T |
JIS H3300 | C7060T |
ASTM B111 | C70600 |
ASTM B466 | C70600 |
BS2871 {PART2} | CN102 |
AS1752 | C70600 |
DIN17664 | CuNi10Fe 1Mn |
DIN 86019 WL2.1972 | CuNi10Fe 1.6Mn |
EEMUA 144 | 7060X |
MIL-T-16420K | 706 |
EN12449 | CW352H |
Tube
Sheet/Plate
SOLID BAR | 1/4" - 12" diameter |
PLATE | up to 6" thick |
Typical Uses for C706 Copper Nickel "90/10"
- Automotive: Power Steering Tube, Brake Lines
- Consumer: Screw Lamp Bases
- Industrial: Condenser Plates, Condensers, Weld Torch Tips, Heat Exchanger Tubes, Valve Bodies, Evaporator Tubes, Pressure Vessels, Distiller Tubes, Pump Impellers for Oil Refining, Ferrules, Evaporators
- Marine: Boat Hulls, Tube Sheet for Salt Water Service, Salt Water Pipe Fittings, Salt Water Piping Systems, Salt Water Piling Wrap, Hot Water Tanks, Salt Water Baffles, Propeller Sleeves, Ship Hulls, Water Hoses
- Plumbing: Flanges
Product Specifications
End Product | Specification |
Bar | ASTM B151, B122, MILITARY MIL-C-15726 |
Pipe, Seamless | ASME SB466, ASTM B466 |
Pipe, Welded | ASME SB467, ASTM B608, B467 |
Plate | ASTM B122, MILITARY MIL-C-15726 |
Plate, Clad | ASTM B432 |
Plate, Condenser Tube | ASME SB171, ASTM B171, SAE J463, J461 |
Rod | ASTM B151, MILITARY MIL-C-15726 |
Rod, Welding | AWS A5.15 |
Sheet | ASTM B122, MILITARY MIL-C-15726, SAE J463, J461 |
Strip | ASTM B122, MILITARY MIL-C-15726 |
Tube, Condenser | ASME SB111, ASTM B552, B111, MILITARY MIL-T-15005, SAE J463, J461 |
Chemical Composition
Cu | Fe | Pb | Mn | Ni | Zn | |
Min/Max | Rem | 1.0 - 1.8 | 0.05 | 1 | 9.0 - 11.0 | 1 |
Nominals | 88.6000 | 1.4000 | - | - | 10.0000 | - |
Temper
Product Type | Temper Type |
Bar | ASTM B151, B122, MILITARY MIL-C-15726 |
Pipe, Seamless | ASME SB466, ASTM B466 |
Pipe, Welded | ASME SB467, ASTM B608, B467 |
Plate | ASTM B122, MILITARY MIL-C-15726 |
Plate, Clad | ASTM B432 |
Plate, Condenser Tube | ASME SB171, ASTM B171, SAE J463, J461 |
Rod | ASTM B151, MILITARY MIL-C-15726 |
Rod, Welding | AWS A5.15 |
Sheet | ASTM B122, MILITARY MIL-C-15726, SAE J463, J461 |
Strip | ASTM B122, MILITARY MIL-C-15726 |
Tube, Condenser | ASME SB111, ASTM B552, B111, MILITARY MIL-T-15005, SAE J463, J461 |
Mechanical Properties
Temper | Sect. Size | Cold Work | Type Min | Temp | Tensile Strength | YS 0.05% UL |
YS 0.02% Offset |
YS 0.005% Offset |
Elong. | RH B |
RH C |
RH F |
RH 30T |
VH 500 |
BH 500 |
BH 3000 |
Shear Strgth |
Fatigue Strgth |
Izod Impact Strgth |
- | in. | % | - | F | ksi | ksi | ksi | ksi | % | B | C | F | 30T | 500 | 500 | 3000 | ksi | ksi | ft-lb |
- | mm. | - | - | C | MPa | MPa | MPa | MPa | - | - | - | - | - | - | - | - | MPa | MPa | J |
Tube | |||||||||||||||||||
OS025 | 0 | 68 | 80 | 16 | - | - | - | - | - | - | - | - | - | - | - | - | |||
OS025 | 0 | 0 | TYP | 20 | 552 | 110 | - | - | 42 | 15 | - | 65 | 26 | - | - | - | - | - | 0 |
H55 | 0 | 68 | 60 | 57 | - | - | - | - | - | - | - | - | - | - | - | - | |||
H55 | 0 | 0 | TYP | 20 | 414 | 393 | - | - | 10 | 72 | - | 100 | 70 | - | - | - | - | - | 0 |
Physical Properties
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 9.5 · 10-6 per oF (68-572 F) | 17.1 · 10-6 per oC (20-300 C) |
Density | 0.323 lb/in3 at 68 F | 8.94 gm/cm3 @ 20 C |
Electrical Conductivity | 9 %IACS @ 68 F | 0.053 MegaSiemens/cm @ 20 C |
Electrical Resistivity | 115.0 ohms-cmil/ft @ 68 F | 19.12 microhm-cm @ 20 C |
Melting Point - Liquidus | 2100 F | 1149 C |
Melting Point - Solidus | 2010 F | 1099 C |
Modulas of Elasticity in Tension | 18000 ksi | 124000 MPa |
Modulus of Rigidity | 6800 ksi | 46880 MPa |
Specific Gravity | 8.94 | 8.94 |
Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg · oK at 293 K |
Thermal Conductivity | 26.0 Btu · ft/(hr · ft2 · oF) at 68F | 45.0 W/m · oK at 20 C |
Fabrication
Joining Technique | Suitability |
Brazing | Excellent |
Butt Weld | Excellent |
Capacity for Being Cold Worked | Good |
Capacity for Being Hot Formed | Good |
Coated Metal Arc Welding | Good |
Gas Shielded Arc Welding | Excellent |
Machinability Rating | 20 |
Oxyacetylene Welding | Fair |
Seam Weld | Good |
Soldering | Excellent |
Spot Weld | Good |
Our Services

Aviva Metals Houston warehouse operation is a AS9120B, and AS9100D in our Ohio foundry, based on ISO 9001:2015. We are now also offering our complete range of brass, bronze and copper alloys in precision machined or milled parts, in full accordance with your drawings. Aviva Metals creates custom precision bearings and bushings, flanges, washers, double flange bearings, full half bearings, spacers and special machined parts that can be shipped on a global basis and in full accordance with most international standards.